Search results

This study aims to investigate the most effective approach for governments and enterprises to combat desertification by considering the governance cycle. The focus is on understanding how the government can incentivize enterprises to actively engage in desertification combat efforts.

Both the government and the enterprise are treated as rational entities, making strategic choices for joint participation in combating desertification. Recognizing the dynamic nature of the desertification combat area, differential game models are employed to identify the optimal mode for combating desertification.

The findings underscore the significant influence of the governance cycle duration on the selection of desertification combat modes for government and enterprise. A cooperative mode is best suited to a short governance cycle, while an ecological subsidy mode is optimal for a longer cycle. Enhancing governance technology and shortening the governance cycle are conducive to combating desertification. Reducing taxes alone may not be an effective control strategy; rather, the government can better motivate enterprises by adopting tax rate policies aligned with the chosen governance mode.

This research contributes by elucidating the impact mechanism of the government cycle’s length on the desertification combat process. The results may offer valuable insights for governments in formulating strategies to encourage corporate participation in combating desertification and provide theoretical support for selecting optimal desertification combat modes.

Due to the harsh underground environment in coal mining, the surface of hydraulic support columns corrodes severely, resulting in significant economic losses. Therefore, a highly corrosion-resistant coatings is needed to extend the service life of the columns.

This study aims to compare the corrosion resistance of ST-Cr₃C₂-NiCr (sealed treatment Cr₃C₂-NiCr) coatings with industrially applied chromium plating. The corrosion failure mechanism of the coatings was investigated.

The results demonstrated that the ST-Cr₃C₂-NiCr coatings exhibited excellent corrosion resistance. After sealing treatment, the corrosion potential of Cr₃C₂-NiCr coatings was −0.215 V, and the corrosion current density of Cr₃C₂-NiCr coatings was lower than that of the plated parts.

ST-Cr₃C₂-NiCr coatings prepared by supersonic atmospheric plasma spraying could provide excellent corrosion resistance in the coal industry.

The low porosity and the presence of the NiCr phase were crucial factors contributing to the preferable corrosion resistance exhibited by the ST-Cr₃C₂-NiCr coatings. The corrosive process of the coatings involved layer-by-layer delamination of surface oxide film, sub-surface pitting, formation and degradation of sub-surface passive film, as well as severe block-like delamination.